Low Shrinkage Polyimide Film 3mil Thickness

Low Shrinkage Polyimide Film 3mil Thickness

Broadly Utilized Polyimide Pi Film with Superb Houses

Software/Model
Our products use to national defense industry aerospace industry, electric motor sector, FPC and TAB of electronic business, Grade H, C insulating components (pulling motor, submersible oil electric motor , nuclear electrical power equipments, higher-temperature-resistant components, special electrical appliances, fire-proofing bus duct, gas mask, loudspeaker voice skeleton), our products polyimide movies as mother or father metal is the very best selection of FPC, PST, versatile copper layer plate, LED and high-temperature insulated supplies. 
Welcome to check with.
 

Things Models Solution model Test Problems CZPT
Thickness   μm 75-76 23ºC ASTM D374
Tensile toughness TD MPa ≥170 23ºC ASTM D882
MD ≥170  
Elongation TD % ≥65 23ºC ASTM D882
MD ≥65  
Young’s Modulus   GPa ≥3.one 23ºC ASTM D882
Dielectric Continuous     three.5±0.4 1MHz 23ºC ASTM D150
Dielectric Dissipaion Element     ≤0.004 1MHz 23ºC ASTM D150
Volume Resisticity   Ω•cm >1012 500V 23ºC ASTM D257
Floor Resistivity   Ω >10fourteen 500V 23ºC ASTM D257
Dielectric Toughness   v/μm ≥200 23ºC ASTM D149
CTE   Ppm/ºC 30±5
30±5
one hundred~200ºC
200~300ºC
ASTM D696
Shrinkage Price   % ≤0.08 200ºC,2Hr ASTM D5213-04
Drinking water Absorption   % ≤2.two 23ºC,soak for 24Hr ASTM D570
Density   g/cm³ one.44±0.two 23ºC ASTM D1505
Wetting Tension   mN/m 60 23ºC IEC674-2

 

Low Shrinkage Polyimide Film 3mil Thickness